Ammonium Polyphosphate (APP) Fire Retardant

• Customization: Available
• Material: APP, PE
• Feature: Photodegradable
• Model NO.: APP
• Usage: General Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Film Pressure
• Color: White
• Einecs: 269-789-9
• CAS No.: 68333-79-9
• Formula: (Nh4po3)N
• Transport Package: 25kg Bags
• Specification: APP
• Trademark: DC
• Origin: China
• HS Code: 28353990
• Production Capacity: 500 Tons Per Month

Product Description

Ammonium polyphosphate (APP) is one kind of non halogen flame retardant. It has extensive possibilities in fire prevention. 
Ammonium polyphosphate(n>1000)
Appearance:white flow powder
 
Properties
P %(w/w) 31.0-32.0
N %(w/w) 14.0-15.0
Ph (10% suspension ) 5.5-7.0
Moisture%(w/w) ≤0.25
decomposed temp. on heat ºC ≥275
density 25ºCkg/L About 1.9
bulk density 25ºCkg/L About 0.7
viscosity (25ºC,10% suspension )mpa.s ≤100
Solubility (g/100cm3 water ) About 0.5
grain sizeum About 15
 
APP is non-tocxic fire retardant, but you should wear defence for it is very tiny powder
 
Uses: APP are used in expanding fire-refractory coating and PU foamalso applied in fiber, wood and plastic rubber. It has high molecular weight (n>1000) and high stability, it can be used in expanding fire-refractory coating
 
Packing:25kg in PE lined woven bag

1.Advantage OF Our Ammonium Polyphosphate

(1)High degree of polymerization up to 1300, excellent performance of fire protection in intumescent systems, has more wide range of application than low polymerization APP.
(2)Initial decomposition temperature 280 degree Celsius, action time earlier than other common ammonium polyphosphate
(3)Low water solubility, high polymerizaiton and intial decompostion temperature make our ammonium polyphosphate good compatibility.

2. Main Application

Ammonium Polyphosate can be used in top-grade fire-retardant coating, fiberglass and engineering plastic, such as PE, PP, PU, polyester and nylon.
(1) With 15-20% APP in the adhesive and sealing agent, the good firing resistance is shown.
(2) For PU, APP is a very suitable preventing form buring dope without halogen.
(3) It is also applicated in hot solidifying resin of epoxy resin or unsaturated resin, etc.

3. Package, transportation and storage

Package: Internal plastic with knitted exterior covered with film, with the net weight of 25kg.
Loading Container: 25kg/bag on pallet, 20metric ton per 20'container
                                500kg/bag on pallet, 15 meric ton per 20"container
Transportation: The product is of dangerous one, which should be protected from damp, rainfall and package damage in transportation.
Storage: At dry warehouse with good ventilation.

4. Specification

Appearance	White Powder	Technical Grade
Test Items	Phase II Standard Value	Result
P2O5     %     ≥	71	73.80
Nitrogen    % ≥	14.0	14.73
Decomposed Temp.on heat^OC           ≥	--	287
Degree of Polymerization               ≥	1000	1300
PH(g/100ml H2O) PH Value	5.5-7.5	5.98
Granularity(through 45μm Testing sieve)  % ≤	20	1.0
Solubility (g/100ml H2O)                    ≤	0.5	0.29
Mositure        % ≤	0.25	0.14
Bulk Density (g/ml)	0.4--0.7	0.38